Chemical Composition Mechanical Property
Grade（材质） | C(%)（碳） | Si(%)（硅） | Mn(%)（锰） | P(%)（磷） | S(%)（硫） | Cr(%)（铬） | Ni(%)（镍） | N(%)（氮） | Cu(%)（铜） |
310 | ≤0.25 | ≤1.0 | ≤2.0 | ≤0.03 | --- | 24.0-26.0 | 19.0-22.0 | --- | --- |
310S | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.03 | ≤0.03 | 24.0-26.0 | 19.0-22.0 | --- | --- |
Grade（材质） | tensile strength Mpa（抗拉强度） | Yield Strength Mpa（屈服强度） | Elongation (%)（伸长率） | rate of reduction in area (%)（断面收缩率） | Density (g/cm3)（密度） |
310 | ≥470 | ≥170 | ≥40 | ≥50 | 7.98 |
310S | ≥520 | ≥205 | ≥40 | ≥50 | 7.98 |
Technical（工艺） | Thickness（厚度） | Width（宽度） | Finish（表面） | Origin（产地） |
Cold rolled | 0.4mm-3.0mm | Standard width in China:1000mm 1219mm 1500mm Special:can be ordered | 2B / No.4 / HL / BA / Mirror etc | TISCO / ZPSS etc |
Hot rolled | 3.0mm-80.0mm | Standard width in China:1219mm 1500mm 2000mm Special:can be ordered | No.1 | TISCO/ZPSS etc |
Applications
310 310S stainless steel is the most common choice of boiler materials. Also widely used in stamping dies, fixtures, tools, gauges, paper cutting knives, tools, petroleum, electronics, chemical, pharmaceutical, textile, food, machinery, construction, nuclear power, aerospace, military and other industries!
201 stainless steel sheet
About 201 /202 stainless steel
201 stainless steel is the most widely used in the 200 series. Because 201 stainless steel With"acid"and "alkali resistance"and"high density", "no bubbles", "no pinhole, polishing".
201 is the choice of all kinds of "watchcase", "watchband bottom”,"decorative tubes", "industrial tubes", and a plurality of products with shallow drawing etc.
Compared with 201 grade,the only difference with 201 is that the Nickle contenting,and with the same applications,characteristic etc.
321 stainless steel sheet
About 321 stainless steel
321 stainless steel belongs to austenitic stainless steel, its performance is very similar to the 304, but due to the addition of the metal titanium, it has a better intergranular corrosion resistance and high temperature strength. The addition of titanium, making it effective control of the formation of chromium carbide.
Excellent high-temperature stress of 321 stainless steel with a breaking (Stress Rupture) properties and high temperature creep resistance (Creep Resistance) stress mechanical properties are superior to 304 stainless steel.
304/304L stainless steel sheet
304/304Lstainless steel
304 304L belongs to austenitic stainless steel, it is the most widely used in the 300 series materials. On the whole, the 304 304L has very similar characteristics, the only difference lies in the level of carbon content, so there will be a little difference more or less in the application filed, but the overall application is the same.
304L has lower carbon content and better corrosion resistance. But 304 of the strength is higher than 304L, so 304 has a higher strength than 304L.From the application: 304 can be widely used in various departments, various fields. 304L is mainly used in welding and other fields.