310/310S stainless steel
310 stainless steel austenitic chromium nickel stainless steel has good oxidation resistance, corrosion resistance, because the higher percentage of chromium and nickel, 310 has much better creep strength, can continuously work under high temperature, good heat resistance.
310S stainless steel is austenitic chromium nickel stainless steel, has a good 310S stainless steel oxidation resistance, resistance Corrosive.
Because of the high percentage of chromium and nickel, which has a much better creep strength, can continue to work at high temperature, with good heat resistance.
Due to the high content of nickel (Ni), chromium (Cr), good oxidation resistance, corrosion resistance, acid and alkali resistance, high temperature resistance, high temperature resistant steel pipe is used in the manufacture of electric furnace tubes and other occasions.
The only differences for 310 310S stainless steel is the 310 stainless steel does not contain sulfur elements.What’s more,the carbon content of 310S is much lower than 310.
Chemical Composition Mechanical Property
Grade（材质） | C(%)（碳） | Si(%)（硅） | Mn(%)（锰） | P(%)（磷） | S(%）（硫） | Cr（%）（铬） | Ni(%)（镍） | N(%)（氮） | Cu(%)（铜） |
310 | ≤0.25 | ≤1.0 | ≤2.0 | ≤0.03 | --- | 24.0-26.0 | 19.0-22.0 | --- | --- |
310S | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.03 | ≤0.03 | 24.0-26.0 | 19.0-22.0 | --- | --- |
Grade（材质） | tensile strength(Mpa)（抗拉强度） | Yield Strength(Mpa)（屈服强度） | Elongation(%)（伸长率） | rate of reduction in area(%)（断面收缩率） | Density(g/cm3)（密度） |
310 | ≥470 | ≥170 | ≥40 | ≥50 | 7.98 |
310S | ≥520 | ≥205 | ≥40 | ≥50 | 7.98 |
Technical（工艺） | Thickness（厚度） | Width（宽度） | Finish（表面） | Origin（产地） |
Cold rolled | 0.4mm-3.0mm | Standard width in China:1000mm 1219mm 1500mm Special:can be ordered | 2B / No.4 / HL / BA / Mirror etc | TISCO / ZPSS etc |
Hot rolled | 3.0mm-80.0mm | Standard width in China:1219mm 1500mm 2000mm Special:can be ordered | No.1 | TISCO/ZPSS etc |
Applications
310 310S stainless steel is the most common choice of boiler materials. Also widely used in stamping dies, fixtures, tools, gauges, paper cutting knives, tools, petroleum, electronics, chemical, pharmaceutical, textile, food, machinery, construction, nuclear power, aerospace, military and other industries!
201 stainless steel plate
About 201 /202 stainless steel
201 stainless steel is the most widely used in the 200 series. Because 201 stainless steel With"acid"and "alkali resistance"and"high density", "no bubbles", "no pinhole, polishing".
201 is the choice of all kinds of "watchcase", "watchband bottom”,"decorative tubes", "industrial tubes", and a plurality of products with shallow drawing etc.
Compared with 201 grade,the only difference with 201 is that the Nickle contenting,and with the same applications,characteristic etc.
321 stainless steel plate
About 321 stainless steel
321 stainless steel belongs to austenitic stainless steel, its performance is very similar to the 304, but due to the addition of the metal titanium, it has a better intergranular corrosion resistance and high temperature strength. The addition of titanium, making it effective control of the formation of chromium carbide.
Excellent high-temperature stress of 321 stainless steel with a breaking (Stress Rupture) properties and high temperature creep resistance (Creep Resistance) stress mechanical properties are superior to 304 stainless steel.
Embossed stainless stee plate