About 201 /202 stainless steel
201 stainless steel is the most widely used in the 200 series. Because 201 stainless steel With"acid"and "alkali resistance"and"high density", "no bubbles", "no pinhole, polishing".
201 is the choice of all kinds of "watchcase", "watchband bottom”,"decorative tubes", "industrial tubes", and a plurality of products with shallow drawing etc.
Compared with 201 grade,the only difference with 201 is that the Nickle contenting,and with the same applications,characteristic etc.
Chemical Composition and Mechanical Property
Grade（材质） | C(%)（碳） | Si(%)（硅） | Mn(%)（锰） | P(%)磷） | S(%)硫） | Cr(%)（铬） | Ni(%)（镍） | N(%)（氮） | Cu(%)（铜） |
201 | ≤0.15 | ≤0.75 | 5.50-7.50 | ≤0.06 | ≤0.03 | 16.0-18.0 | ≤1.0 | ≤0.25 | 0.80-1.50 |
202 | ≤0.15 | ≤0.75 | 5.50-7.50 | ≤0.06 | ≤0.03 | 16.0-18.0 | 0.9-1.0 | ≤0.25 | 0.80-1.50 |
Grade(材质） | TS(Mpa)（抗拉强度） | YS(Mpa)（屈服强度） | El(%)（伸长率） | rate of reduction in area(%)（断面收缩率） | Density(g/cm3)（密度） |
201 | ≥520 | ≥275 | 50-60 | ----- | 7.93 |
202 | ≥520 | ≥275 | 50-60 | ----- | 7.93 |
Technical （工艺） | Thickness （厚度） | Width （宽度） | Finish （表面） | Origin （产地） |
Cold rolled | 0.3mm-3.0mm | Standard in China:1000mm 1219mm 1500mm Special width:Can be ordered | 2B/BA/No.4/HL etc | LISCO TianCheng |
Hot rolled | 3.0mm-10.0mm | Standard size in China:1219mm 1240mm 1500mm Special width:can be ordered | No.1 | LISCO TianCheng |
Application
1) Widely used in All kinds of watchband, watchband bottom cover, high quality materials etc.
2) Also Widely used in the production original material of Decorative tubes, industrial tubes, and some of the products.
3) Applied to high temperature materials. Because high temperature applications require relatively strong resistance to the material to prevent intergranular corrosion at low temperatures.
4) Because the surface can be a variety of surface processing, also widely used in the decoration industry filed.
304/34L stainless steel plate
304/304Lstainless steel
304 304L belongs to austenitic stainless steel, it is the most widely used in the 300 series materials. On the whole, the 304 304L has very similar characteristics, the only difference lies in the level of carbon content, so there will be a little difference more or less in the application filed, but the overall application is the same.
304L has lower carbon content and better corrosion resistance. But 304 of the strength is higher than 304L, so 304 has a higher strength than 304L.From the application: 304 can be widely used in various departments, various fields. 304L is mainly used in welding and other fields.
Embossed stainless stee plate
316/316L stainless steel plate
316/316L stainless steel
About 316 material:316 stainless steel by adding Mo element, the corrosion resistance, and high temperature strength has greatly improved, high temperature can reach 1200-1300 degrees, can be used in severe conditions.Corrosion resistance is better than 304 stainless steel, in pulp and paper production process has good corrosion resistance. And 316 stainless steel is also resistant to erosion of marine and corrosive industrial atmosphere.
About 316L material: 316L stainless steel has a carbon content of less than 316, which is commonly used in pulp and paper equipment heat exchangers, dyeing equipment, film washing equipment, pipelines, coastal areas outside the building materials. Corrosion resistance is better than 316 material.