About 316 material:316 stainless steel by adding Mo element, the corrosion resistance, and high temperature strength has greatly improved, high temperature can reach 1200-1300 degrees, can be used in severe conditions.Corrosion resistance is better than 304 stainless steel, in pulp and paper production process has good corrosion resistance. And 316 stainless steel is also resistant to erosion of marine and corrosive industrial atmosphere.
About 316L material: 316L stainless steel has a carbon content of less than 316, which is commonly used in pulp and paper equipment heat exchangers, dyeing equipment, film washing equipment, pipelines, coastal areas outside the building materials. Corrosion resistance is better than 316 material.
Chemical Composition and Mechanical Property
Grade （材质） | C(%) （碳） | Si(%) （硅） | Mn(%) （锰） | P(%) （磷） | S(%) （硫） | Cr(%) （铬） | Ni(%) （镍） | Mo(%) （钼） | Cu(%) （铜） |
316 | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 16.0-18.0 | 10.0-14.0 | 2.0-3.0 | ---- |
316L | ≤0.03 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 16.0-18.0 | 10.0-14.0 | 2.0-3.0 | ---- |
Grade （材质） | tensile strength Mpa （抗拉强度） | Yield Strength Mpa （屈服强度） | Elongation (%) （伸长率） | rate of reduction in area (%) （断面收缩率） | Density (g/cm3) （密度） |
316 | ≥520 | ≥205 | ≥40 | ≥60 | 7.98 |
316L | ≥480 | ≥177 | ≥40 | ≥60 | 7.98 |
Specifications
Technical （工艺） | Thickness （厚度） | Width （宽度） | Finish （表面） | Origin （产地） |
Cold rolled | 0.4mm-6.0mm | Standard width in China:1000mm 1219mm 1500mm Special width:can be ordered | 2B / No.4 / HL / BA / Mirror etc | TISCO / ZPSS . JISCO / Baosteel etc |
Hot rolled | 3.0mm-80.0mm | Standard width in China: 1219mm 1500mm 1800mmm 2000mm Specail width:can be ordered | No.1 | TISCO / ZPSS / JISCO etc |
Applications
316 and 316L stainless steel is widely used in pulp and paper equipment heat exchangers, dyeing equipment, film washing equipment, pipelines, coastal areas outside the building materials, marine, industrial air field.Also used in the field of solenoid valve, mainly used in the shell, clamp, ball, valve body, valve seat, nut, stem and so on.
316L stainless steel also has good resistance to chloride corrosion, so it is often used in marine environment.What’s more,with good welding performance, can use all standard welding method for welding.
The Different Standards
Small tips for stainless steel -Finish processing
BA - excellent surface gloss, high reflectivity, like a mirror surface, so it is also called a mirror surface.
1D surface has discontinuous granular, also known as fog surface.
2D - a slightly shiny silver white.
2B - silver and better gloss and flatness than the 2D surface.
No.3 - good gloss and rough surface.
No.4 - good gloss and fine lines on the surface.
HL - silver gray with hairline stripes. Wait.
304/304Lstainless steel coil
201 stainless steel is the most widely used in the 200 series. Because 201 stainless steel With"acid"and "alkali resistance"and"high density", "no bubbles", "no pinhole, polishing". 201 is the choice of all kinds of "watchcase", "watchband bottom”,"decorative tubes", "industrial tubes", and a plurality of products with shallow drawing etc. Compared with 201 grade,the only difference with 201 is that the Nickle contenting,and with the same applications,characteristic etc.
321 stainless steel coil
321 stainless steel belongs to austenitic stainless steel, its performance is very similar to the 304, but due to the addition of the metal titanium, it has a better intergranular corrosion resistance and high temperature strength. The addition of titanium, making it effective control of the formation of chromium carbide. Excellent high-temperature stress of 321 stainless steel with a breaking (Stress Rupture) properties and high temperature creep resistance (Creep Resistance) stress mechanical properties are superior to 304 stainless steel.
310/310S stainless steel coil
310/310S stainless steel
310 stainless steel austenitic chromium nickel stainless steel has good oxidation resistance, corrosion resistance, because the higher percentage of chromium and nickel, 310 has much better creep strength, can continuously work under high temperature, good heat resistance.
310S stainless steel is austenitic chromium nickel stainless steel, has a good 310S stainless steel oxidation resistance, resistance Corrosive.
Because of the high percentage of chromium and nickel, which has a much better creep strength, can continue to work at high temperature, with good heat resistance.
Due to the high content of nickel (Ni), chromium (Cr), good oxidation resistance, corrosion resistance, acid and alkali resistance, high temperature resistance, high temperature resistant steel pipe is used in the manufacture of electric furnace tubes and other occasions.
The only differences for 310 310S stainless steel is the 310 stainless steel does not contain sulfur elements.What’s more,the carbon content of 310S is much lower than 310.